Impact Properties of Low Activation Vanadium Alloy After Low-Temperature Neutron Irradiation at 450°C and Below

Takuya Nagasaka, Takeo Muroga, Takeshi Miyazawa, Hideo Watanabe, Masanori Yamazaki

Fusion Science and Technology / Volume 60 / Number 1 / Pages 379-383

July 2011

Format:

Price:$30.00
Member Price:$27.00
Member Savings:$3.00

A reference low-activation vanadium alloy NIFS-HEAT-2 was neutron-irradiated at 450 °C and below, in order to estimate the resistance to low temperature irradiation. DBTT of NIFS-HEAT-2 was -85 °C after irradiation up to 8.5 dpa at 450 °C in Na atmosphere, while DBTT was below -196 °C for 3.7 dpa at 430 °C in Li atmosphere. On the other hand, DBTT was lower than about -90 °C for the irradiation up to 0.1~1 dpa at 60, 290 and 400 °C. The DBTT shift was increased with increasing hardness after neutron irradiation for limited irradiation conditions. The mechanisms of DBTT shift and irradiation hardening at low temperature was discussed.

 
 
 
Questions or comments about the site? Contact the ANS Webmaster.
advertisement