Charpy Impact Properties of Reduced-Activation Ferritic/Martensitic Steels Irradiated in HFIR up to 20 dpa
Volume 44 · Number 1 · July 2003 · Pages 206-210
Technical Paper · Fusion Energy - Fusion Materials
H. Tanigawa, K. Shiba, M. A. Sokolov, R. L. Klueh
ANS Store: Purchase Article
The effects of irradiation up to 20 dpa on the Charpy impact properties of reduced-activation ferritic/martensitic steels (RAFs) were investigated. The ductile-brittle transition temperature (DBTT) of F82H-IEA shifted up to around 323K. TIG weldments of F82H showed a fairly small variation on their impact properties. A finer prior austenite grain size in F82H-IEA after a different heat treatment resulted in a 20K lower DBTT compared to F82H-IEA after the standard heat treatment, and that effect was maintained even after irradiation. Helium effects were investigated utilizing Ni-doped F82H, but no obvious evidence of helium effects was obtained. ORNL9Cr-2WVTa and JLF-1 steels showed smaller DBTT shifts compared to F82H-IEA.
|
|
|
|