ANS is committed to advancing, fostering, and promoting the development and application of nuclear sciences and technologies to benefit society.
Explore the many uses for nuclear science and its impact on energy, the environment, healthcare, food, and more.
Division Spotlight
Mathematics & Computation
Division members promote the advancement of mathematical and computational methods for solving problems arising in all disciplines encompassed by the Society. They place particular emphasis on numerical techniques for efficient computer applications to aid in the dissemination, integration, and proper use of computer codes, including preparation of computational benchmark and development of standards for computing practices, and to encourage the development on new computer codes and broaden their use.
Meeting Spotlight
2024 ANS Annual Conference
June 16–19, 2024
Las Vegas, NV|Mandalay Bay Resort and Casino
Standards Program
The Standards Committee is responsible for the development and maintenance of voluntary consensus standards that address the design, analysis, and operation of components, systems, and facilities related to the application of nuclear science and technology. Find out What’s New, check out the Standards Store, or Get Involved today!
Latest Magazine Issues
Apr 2024
Jan 2024
Latest Journal Issues
Nuclear Science and Engineering
May 2024
Nuclear Technology
Fusion Science and Technology
Latest News
X-energy receives federal tax credit for TRISO fuel facility
Advanced reactor company X-energy has been awarded $148.5 million in tax credits under the Inflation Reduction Act for construction of its TRISO-X fuel fabrication facility in Oak Ridge, Tenn.
Dennis L. Youchison, Radmir N. Guiniatouline, Robert D. Watson, Jimmie M. McDonald, David S. Walsh, V. I. Beloturov, Igor V. Mazul, Andrey P. Zakharov, Bernice E. Mills, Dale R. Boehme, Vladislav Ilich Savenko
Fusion Science and Technology | Volume 29 | Number 4 | July 1996 | Pages 599-614
Technical Paper | Divertor System | doi.org/10.13182/FST96-A30701
Articles are hosted by Taylor and Francis Online.
Thermal response and thermal fatigue tests of four 5-mm-thick beryllium tiles on a Russian Federation International Thermonuclear Experimental Reactor (ITER)-relevant divertor mock-up were completed on the electron beam test system at Sandia National Laboratories. The beryllium tiles were diffusion bonded onto an oxygen-free high-conductivity copper saddle-block and a dispersion-strengthened copper alloy tube containing a copper porous coating. Thermal response tests were performed on the tiles to an absorbed heat flux of 5 MW/m2 and surface temperatures near 300°C using 1.4 MPa water at 5 m/s flow velocity and an inlet temperature of 8 to 15°C. One tile was exposed to incrementally increasing heat fluxes up to 9.5 MW/m2 and surface temperatures up to 690°C before debonding at 10 MW/m2. A second tile debonded in 25 to 30 cycles at <0.5 MW/m2. However, a third tile debonded after 9200 thermal fatigue cycles at 5 MW/m2, while another debonded after 6800 cycles. Posttest surface analysis indicated that fatigue failure occurred in the intermetallic layers between the beryllium and copper. No fatigue cracking of the bulk beryllium was observed. It appears that microcracks growing at the diffusion bond produced the observed gradual temperature increases during thermal cycling. These experiments indicate that diffusion-bonded beryllium tiles can survive several thousand thermal cycles under ITER-relevant conditions. However, the reliability of the diffusion-bonded joint remains a serious issue.